interfacial agent meaning in Chinese
界面活性剂
Examples
- Effect of interfacial agent on bond strength between new and old concrete
界面剂对新老砼粘结强度的影响 - The main content is : splitting tensile experiments were carried out about the standardized cube bonding specimens ( 150x 150x 150mm3 ) of the new - old concrete after high temperature . the temperature is divided into 9 groups from normal atmospheric temperature to 900 , the cooling styles are natural cooling and spraying water cooling ; different interfacial treating methods : brushed with steel - wire brush , man - made chiseling ( not evenly ) , man - made chiseling ( quite evenly ) ; different interfacial agents : no interfacial agent , neat cement paste , cement paste mixed with 10 % expanding agent
主要内容有：本文对75个高温作用后的标准立方体新老混凝土粘结试件进行了劈拉试验，温度从常温到900c分9个温度段，降温方式分自然冷却和喷水冷却两种。着重考察了温度、降温方式、界面粗糙度及界面剂对新老混凝土粘结劈拉强度的影响规律，阐述了高温后粘结强度下降的机理。 - ( 2 ) interfacial agents this experiment adopts three types of interfacial agents : no interfacial agent , neat cement paste which has the same water - cement ratio with the new concrete , cement paste mixed with 10 % expanding agent which has the same ratio with the new concrete ( which is called cement paste mixed with expanding agent for short ) . the thickness of the interfacial agent is 2 ~ 3mm
（ 2 ）粘结剂本试验采用三种粘结剂：无粘结剂、同新混凝土相同水灰比的水泥净浆、掺10 u型膨胀剂的同新混凝土相同水灰比的水泥净浆（以下简称水泥膨浆） 。界面剂的厚度一般为2 3mm 。 - The matrix phase , interface phase , compound result , and the performance of the straw plant fiber cement composite material was studied , the result shows , under the use of interfacial agent , the good interfacial effect was made between straw plant fiber and cement
摘要对秸秆纤维水泥复合材料的基体相、界面相、复合效果、秸秆纤维水泥基复合材料性能，以及界面剂对其性能的影响等方面进行了研究，结果表明，在界面剂的作用下，秸秆植物纤维和水泥之间取得了良好的界面效果。